GREENSEAL 2K REPAIR MORTAR.

Description

Greenseal 2K Repair Mortar is a 2 components modified repair mortar. It is suitable to be applied on to concrete and mortar to fill and seal pores and voids, crack and hair line of all substrates and yet provides a protective layer which resistant to water and moisture.

USES
Greenseal 2K Repair Mortar consists of organic silica, for cement mortar with low water absorption to achieve waterproofing effect. It can be used as repair mortar with high compressive strength.
It is a 2 components flexible cementitious repair mortar, suitable use in:

1. Bathrooms, toilet and kitchens
2. Balconies and planter boxes
3. Swimming pools
4. Light vehicular traffic

APPLICATION INSTRUCTIONS
Surface Preparation

1. Substrates to be applied with Greenseal 2K repair Mortar must be clean and free from laitance, protrusions, loose particle, dirt, oil and grease.
2. Sharp edges must be flattened and uneven surfaces must be leveled or repaired with a mortar screed by using Greenseal Injection Grout.
3. Cleaned and properly repaired surface must be thoroughly saturated with water.
4. Take caution: No standing water or excessive water shall be remained on the substrate that to be applied with Greenseal 2K Mortar.

MIXING
Greenseal 2K Repair Mortar is supplied in 2 components. Mix the 7.55kg of polymer with the 25kg of Greenseal 2k Repair Mortar. Use a stirrer to stir the mixture until the mixture is free from lumps.

APPLICATION
Apply Greenseal 2K Repair Mortar with a stiff brush, trowel or spray onto the prepared surface. For large space, spray is recommended by using a worm-gear type of spray equipment. For best result, apply Greenseal 2K Repair Mortar under shaded shelter to prevent rapid drying of the coating.

CURING
The freshly applied Greenseal 2K Repair Mortar shall be protected from direct rain, dirt, oil, grease or other loose particle for at least 12 hours. It is foot trafficable after 24 hours and resistant to light mechanical stress after 7 days. Permanent water pressure resistance shall be achieved after a full hardening of 28 days.